Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(American Institute of Physics, 2007-04-27)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(American Institute of Physics, 2007-08-30)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied Physics, 2008-02-08)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(American Institute of Physics, 2007-07-23)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(AIP, 2007)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
High thermal stability of carbon-coated L10-FePt nanoparticles prepared by salt-matrix annealing
(AIP, 2008)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...