Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(American Institute of Physics, 2007-04-27)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Rapid thermal annealing of FePt nanoparticles
(American Institute of Physics, 2008-07-11)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(American Institute of Physics, 2007-08-30)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied Physics, 2008-02-08)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(American Institute of Physics, 2007-07-23)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE XploreIEEE, 2009-07)
Isolated monodisperseL10 FePt nanoparticles coated
by carbon were obtained by adding enough surfactants that decomposed
into carbon after the chemical synthesis and postannealing
of the A1 FePt nanoparticles. The effect ...
Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(AIP, 2007)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Rapid thermal annealing of FePt nanoparticles
(AIP, 2008-07-01)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...