Observation of L1[subscript]0-like chemical ordering in a decahedral FePt nanoparticle by C[subscript]s-corrected high resolution transmission electron microscopy
(American Institute of Physics, 2009-03-09)
The state of the chemical ordering in a decahedral FePt nanoparticle was studied using aberration corrected high resolution transmission electron microscopy. With the reduced image delocalization effect as a result of ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(American Institute of Physics, 2007-08-30)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied Physics, 2008-02-08)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Microstructures and magnetic alignment of L10 FePt nanoparticles
(AIP, 2009)
Chemically ordered FePt nanoparticles were obtained by high temperature annealing a mixture of FePt particles with NaCl. After the NaCl was removed with de-ionized water, the transformed FePt nanoparticles were redispersed ...
High thermal stability of carbon-coated L10-FePt nanoparticles prepared by salt-matrix annealing
(AIP, 2008)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...