Effects of particle size and composition on coercivity of Sm–Co nanoparticles prepared by surfactant-assisted ball milling
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2010-04-15)The correlation between the recoil loop openness and the activation volume has been studied for the SmCo5/α-Fe nanocomposite powder material prepared by mechanical alloying. The α-Fe phase content in the nanocomposite ... -
Mechanism of the anomalous temperature dependence of coercivity in Sm(Co, Fe, Cu, Zr)z high temperature magnets
(AIP, 2006)Coercivity mechanism of the precipitation-hardened Sm Co,Fe,Cu,Zr z high-temperature magnets was found to vary with temperature by measurements of reversible magnetization. The magnetization reversal is mainly controlled ... -
Mechanism of the anomalous temperature dependence of coercivity in Sm(Co,Fe,Cu,Zr)[subscript]z high-temperature magnets
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2006-01-24)Coercivity mechanism of the precipitation-hardened Sm(Co,Fe,Cu,Zr)z high-temperature magnets was found to vary with temperature by measurements of reversible magnetization. The magnetization reversal is mainly controlled ... -
Microstructures and magnetic alignment of L10 FePt nanoparticles
(AIP, 2009)Chemically ordered FePt nanoparticles were obtained by high temperature annealing a mixture of FePt particles with NaCl. After the NaCl was removed with de-ionized water, the transformed FePt nanoparticles were redispersed ... -
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEEDepartment of Physics, The University of Texas at Arlington, 2009-03-31)Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ... -
Rapid thermal annealing of FePt nanoparticles
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2008-07-11)We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ... -
Rapid thermal annealing of FePt nanoparticles
(AIP, 2008-07-01)We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ... -
Shape control of FePt nanocrystals
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2009-04-06): FePt nanocrystals were prepared by simultaneous reduction of platinum acetylacetonate and thermal decomposition of iron pentacarbonyl in properly chosen solvents/surfactants. A variety of FePt nanocrystals, including ...