Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2007-07-23)High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ... -
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ... -
Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2007-04-27)FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ... -
Curie temperatures of annealed FePt nanoparticle systems
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2007-03-28)The chemically synthesized FexPt100-x nanoparticles with controlled compositions were annealed to transfer the disordered face-centered-cubic structure to the ordered structure. It was found that the L10 FePt structure can ... -
Do thermal fluctuations influence the recoil loops of nanocomposite magnets?
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2008-07-11)An exchange-coupled FePt/Fe3Pt nanocomposite system with well defined hard/soft two-phase morphology was prepared by reducing chemically synthesized FePt/Fe3O4 bimagnetic nanoparticles. It was interesting to observe that ... -
Fabrication of bulk nanocomposite magnets via severe plastic deformation and warm compaction,
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2010-03-10)We demonstrate that a SmCo/FeCo based hard/soft nanocomposite material can be fabricated by distributing the soft magnetic α-Fe phase particles homogeneously in a hard magnetic SmCo phase through severe plastic deformation. ... -
High thermal stability of carbon-coated L10-FePt nanoparticles prepared by salt-matrix annealing
(AIP, 2008)Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ... -
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied PhysicsDepartment of Physics, The University of Texas at Arlington, 2008-02-08)Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ... -
Mechanism of the anomalous temperature dependence of coercivity in Sm(Co, Fe, Cu, Zr)z high temperature magnets
(AIP, 2006)Coercivity mechanism of the precipitation-hardened Sm Co,Fe,Cu,Zr z high-temperature magnets was found to vary with temperature by measurements of reversible magnetization. The magnetization reversal is mainly controlled ... -
Mechanism of the anomalous temperature dependence of coercivity in Sm(Co,Fe,Cu,Zr)[subscript]z high-temperature magnets
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2006-01-24)Coercivity mechanism of the precipitation-hardened Sm(Co,Fe,Cu,Zr)z high-temperature magnets was found to vary with temperature by measurements of reversible magnetization. The magnetization reversal is mainly controlled ... -
Observation of L1[subscript]0-like chemical ordering in a decahedral FePt nanoparticle by C[subscript]s-corrected high resolution transmission electron microscopy
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2009-03-09)The state of the chemical ordering in a decahedral FePt nanoparticle was studied using aberration corrected high resolution transmission electron microscopy. With the reduced image delocalization effect as a result of ... -
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2007-08-30)FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ... -
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(AIP, 2007)FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ... -
Temperature- and magnetic-field-induced phase transitions in Fe-rich FePt alloys
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2007-06-01)Structural and magnetic properties of the FexPt100-x (x=78–88) alloys have been investigated. It is found that for all of the investigated compositions, a phase transition occurs from the disordered γ phase to the ordered ... -
Transformation of electrical transport from variable range hopping to hard gap resistance in Zn[subscript]1−[subscript]xFe[subscript]xO[subscript]1[subscript]v magnetic semiconductor films
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2006-11-16)Transformation of the electrical transport from the Efros and Shklovskii [J. Phys. C 8, L49 (1975)] variable range hopping to the “hard gap” resistance was experimentally observed in a low temperature range as the Fe ...