Curie temperatures of annealed FePt nanoparticle systems
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2007-03-28)The chemically synthesized FexPt100-x nanoparticles with controlled compositions were annealed to transfer the disordered face-centered-cubic structure to the ordered structure. It was found that the L10 FePt structure can ... -
Effects of particle size and composition on coercivity of Sm–Co nanoparticles prepared by surfactant-assisted ball milling
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2010-04-15)The correlation between the recoil loop openness and the activation volume has been studied for the SmCo5/α-Fe nanocomposite powder material prepared by mechanical alloying. The α-Fe phase content in the nanocomposite ... -
Microstructures and magnetic alignment of L10 FePt nanoparticles
(AIP, 2009)Chemically ordered FePt nanoparticles were obtained by high temperature annealing a mixture of FePt particles with NaCl. After the NaCl was removed with de-ionized water, the transformed FePt nanoparticles were redispersed ... -
Shape control of FePt nanocrystals
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2009-04-06): FePt nanocrystals were prepared by simultaneous reduction of platinum acetylacetonate and thermal decomposition of iron pentacarbonyl in properly chosen solvents/surfactants. A variety of FePt nanocrystals, including ...