Microstructures and magnetic alignment of L10 FePt nanoparticles
(AIP, 2009)Chemically ordered FePt nanoparticles were obtained by high temperature annealing a mixture of FePt particles with NaCl. After the NaCl was removed with de-ionized water, the transformed FePt nanoparticles were redispersed ... -
Observation of L1[subscript]0-like chemical ordering in a decahedral FePt nanoparticle by C[subscript]s-corrected high resolution transmission electron microscopy
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2009-03-09)The state of the chemical ordering in a decahedral FePt nanoparticle was studied using aberration corrected high resolution transmission electron microscopy. With the reduced image delocalization effect as a result of ... -
Rapid thermal annealing of FePt nanoparticles
(American Institute of PhysicsDepartment of Physics, The University of Texas at Arlington, 2008-07-11)We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ... -
Rapid thermal annealing of FePt nanoparticles
(AIP, 2008-07-01)We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...