Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(AIP, 2007)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
Rapid thermal annealing of FePt nanoparticles
(AIP, 2008-07-01)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...
High thermal stability of carbon-coated L10-FePt nanoparticles prepared by salt-matrix annealing
(AIP, 2008)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...