Observation of L1[subscript]0-like chemical ordering in a decahedral FePt nanoparticle by C[subscript]s-corrected high resolution transmission electron microscopy
(American Institute of Physics, 2009-03-09)
The state of the chemical ordering in a decahedral FePt nanoparticle was studied using aberration corrected high resolution transmission electron microscopy. With the reduced image delocalization effect as a result of ...
Bimagnetic nanoparticles with enhanced exchange coupling and energy products
(American Institute of Physics, 2009-01-06)
Bimagnetic FePt/Fe3O4 nanoparticles with core/shell or heterodimer structure have been prepared using a sequential synthetic method. The dimension of both FePt and Fe3O4 was tuned by varying the synthesis parameters. The ...
Rapid thermal annealing of FePt nanoparticles
(American Institute of Physics, 2008-07-11)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(American Institute of Physics, 2007-08-30)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied Physics, 2008-02-08)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...
Curie temperatures of annealed FePt nanoparticle systems
(American Institute of Physics, 2007-03-28)
The chemically synthesized FexPt100-x nanoparticles with controlled compositions were annealed to transfer the disordered face-centered-cubic structure to the ordered structure. It was found that the L10 FePt structure can ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(American Institute of Physics, 2007-07-23)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Do thermal fluctuations influence the recoil loops of nanocomposite magnets?
(American Institute of Physics, 2008-07-11)
An exchange-coupled FePt/Fe3Pt nanocomposite system with well defined hard/soft two-phase morphology was prepared by reducing chemically synthesized FePt/Fe3O4 bimagnetic nanoparticles. It was interesting to observe that ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...