Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(American Institute of Physics, 2007-04-27)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Effect of thermal fluctuations on the recoil loops of SmCo5[subscript]/Fe nanocomposite system
(American Institute of Physics, 2009-02-13)
The correlation between the recoil loop openness and the activation volume has been studied for the SmCo5/α-Fe nanocomposite powder material prepared by mechanical alloying. The α-Fe phase content in the nanocomposite ...
Bimagnetic nanoparticles with enhanced exchange coupling and energy products
(American Institute of Physics, 2009-01-06)
Bimagnetic FePt/Fe3O4 nanoparticles with core/shell or heterodimer structure have been prepared using a sequential synthetic method. The dimension of both FePt and Fe3O4 was tuned by varying the synthesis parameters. The ...
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied Physics, 2008-02-08)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...
Shape control of FePt nanocrystals
(American Institute of Physics, 2009-04-06)
: FePt nanocrystals were prepared by simultaneous reduction of platinum acetylacetonate and thermal decomposition of iron pentacarbonyl in properly chosen solvents/surfactants. A variety of FePt nanocrystals, including ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
High thermal stability of carbon-coated L10-FePt nanoparticles prepared by salt-matrix annealing
(AIP, 2008)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...