Shape control of FePt nanocrystals
(American Institute of Physics, 2009-04-06)
: FePt nanocrystals were prepared by simultaneous reduction of platinum acetylacetonate and thermal decomposition of iron pentacarbonyl in properly chosen solvents/surfactants. A variety of FePt nanocrystals, including ...
Mechanism of the anomalous temperature dependence of coercivity in Sm(Co,Fe,Cu,Zr)[subscript]z high-temperature magnets
(American Institute of Physics, 2006-01-24)
Coercivity mechanism of the precipitation-hardened Sm(Co,Fe,Cu,Zr)z high-temperature magnets was found to vary with temperature by measurements of reversible magnetization. The magnetization reversal is mainly controlled ...
Do thermal fluctuations influence the recoil loops of nanocomposite magnets?
(American Institute of Physics, 2008-07-11)
An exchange-coupled FePt/Fe3Pt nanocomposite system with well defined hard/soft two-phase morphology was prepared by reducing chemically synthesized FePt/Fe3O4 bimagnetic nanoparticles. It was interesting to observe that ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE XploreIEEE, 2009-07)
Isolated monodisperseL10 FePt nanoparticles coated
by carbon were obtained by adding enough surfactants that decomposed
into carbon after the chemical synthesis and postannealing
of the A1 FePt nanoparticles. The effect ...
Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(AIP, 2007)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(AIP, 2007)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
Rapid thermal annealing of FePt nanoparticles
(AIP, 2008-07-01)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...
High thermal stability of carbon-coated L10-FePt nanoparticles prepared by salt-matrix annealing
(AIP, 2008)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...